目的 通过比较二胎孕妇和初产孕妇心电图变化探讨其对妊娠结局的影响。方法 随机选取300例孕妇,其中150例二胎孕妇为观察组,150例初产孕妇为对照组。观察2组孕妇异常心电图的类型及发生率,分析异常心电图与妊娠结局的关系。结果 初产孕妇组异常心电图35例,心电图异常发生率为23.3%,二胎孕妇组异常心电图50例,心电图异常发生率为33.3%,两组心电图异常发生率差别有统计学意义(P<0.05)。二胎孕妇组窦性心动过速、室性早搏及ST-T改变的发生率显著高于初产孕妇组,差异有统计学意义(P<0.05)。二胎孕妇心电图异常组的剖宫产率和早产率均高于二胎孕妇心电图正常组、初产孕妇心电图正常组,差别有统计学意义(P>0.05)。结论 二胎孕妇易合并心电图异常改变,心电图异常会增加剖宫产和早产的发生率,临床医生在诊治此类患者时应提高警惕。

Objective To observe the relationship between electrocardiogram(ECG) and pregnancy outcomes of the second pregnant women. Methods Pregnant women were divided into two groups by parity history: the second pregnancy group and the Primipara group. The incidence of abnormal electrocardiogram was recorded, then the pregnancy outcome including the delivery mode and the premature birth rate were followed up. Results The incidence of abnormal ECG in the second pregnancy group was significantly higher than that in primipara group(P<0.05) and the incidences of Nodal tachycardia, Premature ventricular contraction, ST-T changes in the group of the second pregnancy were higher than that in the group of Primipara (P<0.05). The incidence of cesarean delivery and premature birth in the second pregnancy group with abnormal ECG group was significantly higher than that in pregnant women with normal ECG group (P<0.05). Conclusion The second pregnant women are more likely to have ECG abnormality, the pregnant women with abnormal ECG are easily suffer from cesarean delivery and premature birth.

目的 体外构建胶原—壳聚糖复合支架材料,分析其物理化学性质及生物相容性,探讨其应用于组织工程支架材料的可行性。方法 利用冷冻干燥的方法构建三维多孔的胶原支架材料,通过甲醛交联以及添加壳聚糖的方法改善其物理化学性能。通过体外降解实验以及电镜扫描的方法检测材料的各项物理化学指标;通过细胞接种的方法研究材料的生物相容性。结果 胶原—壳聚糖复合材料通过冷冻干燥的方法,能够获得稳定的三维多孔结构,电镜显示孔隙贯通,体外降解速度降低,并且能够支持细胞生长。理化性质分析显示该结构适合细胞生长,具有良好的生物相容性。结论 本课题体外构建胶原—壳聚糖复合支架材料,满足组织工程生物材料的理化以及生物相容性要求,为其应用于组织工程支架材料提供重要的依据。

Objective We build up the Collagen-Chitosan compound scaffold in vitro,and study the physical,chemical and biological properties,to analyze the feasibility in tissue engineering. Methods The three-dimensional porous scaffold was obtained by freezing-drying method,and optimized by using formaldehyde and Chitosan.We used hydrolysis in vitro and SEM scanning to investigate its physical and chemical properties.The biocompatibility of scaffold was analyzed in MEF cells. Results Collagen-Chitosan compound scaffold we obtained by freezing-drying method was a kind of stable 3D vesicular structure.The scaffold degenerated in decreased velocity in vitro.The physical and chemical properties showed that it was suitable for the cells grow in it,which suggested that it has a good biocompatibility. Conclusion This kind of Collagen-Chitosan compound scaffold is constructed.It's qualified by the physical and chemical properties,and biocompatibility which the biomaterials require.The evidence are important for its application in tissue engineering.